Clean, dust-free and capable of supporting a load.

Substrate: absorbent with low strength

Apply product as a bonding layer > 50% opaque.

Substrate: weakly absorbent

Apply product as a scratch coat (contact layer).

Temperature of the material, air and substrate: from min. +5 °C to max. +30 °C

Apply mortar by hand; for layer thicknesses greater than 15 mm, throw on or apply using a rendering machine.

Maximum layer thickness approx. 20 mm (depending on the specific formulation).

Once it has hardened, mortar must not be made workable again by adding either water or more wet mortar.

Protect wet mortar surfaces against frost, rain and drying out too quickly for at least 4 days.

Hairline/shrinkage cracks are safe and are not cause for complaint as they do not impair the properties of the mortar.

Since the material is formulated for a specific object, application by machine cannot be guaranteed.

Mixer, trowel, smoothing trowel, aluminium float, render comb, sponge float

Clean tools with water while the material is still fresh.

Dry, in unopened containers, 6 months.

Dependent on building and formulation

Apply to a large enough trial area to determine the precise amount required.

The mixing water must be of drinking water quality.

May contain traces of pyrite (iron sulphide).

Do not use on gypsum-based substrates.

Low chromate content in accordance with Directive 2003/53/EC.

The characteristic data of the product were calculated under laboratory conditions at 20°C and 65% relative humidity.

Larger quantities of leftover product should be disposed of in the original containers in accordance with the applicable regulations. Completely empty, clean containers should be recycled. Do not dispose of together with household waste. Do not allow to enter the sewage system. Do not empty into drains.